ACIDITY, SOLUBILITY AND CHEMICAL UTILIZATION OF LOCAL LEUCAENA LEUCOCEPHALA STEM BARK
Rafidah Salim1,2*, Jahimin Asik2 and Mohd Sani Sarjadi2
1Wood Chemistry Laboratory, Faculty of Science and Natural Resources, Universiti Malaysia Sabah, 88400 Kota Kinabalu, Sabah, Malaysia
2Industrial Chemistry Programme, Faculty of Science and Natural Resources, Universiti Malaysia Sabah, 88400 Kota Kinabalu, Sabah, Malaysia
*Corresponding Author Email: firstname.lastname@example.org, email@example.com
This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Acidity, solubility and chemical properties of eleven years old of Leucaena leucocephala stem bark were investigated. The bark was peeled from the stem of tree and gentle washed in tap water to remove dirt before air-dried in the laboratory at room temperature (24 + 3°C) for 2-3 weeks. The bark was minced into coarse powder and grind to pass BS 250µm mesh sieve. After air-dried for several days, the samples were conducted to chemical analyses (ash content and pH value; solubility in 1%NaOH, hot and cold water solubility; extractive, cellulose and lignin content) based on ASTM standard methods. The results show that L. leucocephala stem bark considered as least acidic (pH value 6.04) and high ash content (15.76%). The solubility of bark components was higher in 1% NaOH (41.36%) compared to hot water (14.45%) and cold water (11.06%). Holocellulose and hemicellulose was 132.85% and 103.66%, respectively. Lignin was the major composition in L. leucocephala stem bark (38.4%) followed by cellulose (29.19%) and extractive (8.39%). This study indicated that the bark of L. leucocephala had less acidity. The high solubility of the bark potential as a carbohydrate resource, while the chemical component of the bark might influence rapid combustion during pyrolysis.